Product Information
Terluran庐 HI-12
Mar. 2006
Product description
Injection moulding grade with a very high toughness and easy flow
Applications
Home appliances, E/E application, helmet, heel top, motor bicycle parts etc.
Physical form and storage
Terluran is delivered in the form of cylindrical or spherical pellets. The bulk
density of the pellets is from 0.55 to 0.65 g/cm鲁. Values may differ for special
grades. Standard Packaging unit: 25 kg paper bag. In addition, delivery in larger
units of up to 1000 kg (IBC = Intermediate Bulk Container) or silo trucks can be
arranged.
In dry areas with normal temperature control, Terluran pellets can be stored for
relatively long periods of time without any change in mechanical properties.
With unstable colours, however, storage over a number of years can give rise to
some change in colour. Under poor storage conditions, Terluran absorbs
moisture, but this can be removed by drying.
Product safety
No adverse effects on the health of processing personnel have been observed
where the products are correctly processed and the production areas are
suitably ventilated. For styrene, alpha-methylstyrene, acrylonitrile, and 1,3-
butadiene the maximum allowable workplace concentrations must be observed
according to the pertaining national regulations. In Germany, the following limit
values are valid (Nov 1999): styrene, MAK-value: 20 ml/m鲁 = 85 mg/m鲁;
alpha-methylstyrene, MAK-value: 100 ml/m鲁 = 480 mg/m鲁; acrylonitrile, TRK-
value: 3 ml/m鲁 = 7 mg/m鲁 and 1,3-butadiene, TRK-value: 5 ml/m鲁 = 11
mg/m鲁. According to EU directive 67/548/EEC, Annex I (Nov 1999), acrylonitrile
and 1,3-butadiene are classified as carcinogenic, category 2 ( 'substances
which should be regarded as if they are carcinogenic to man'). Experience has
shown that when Terluran is processed correctly with appropriate ventilation, the
levels are far below the limits mentioned above. Inhalation of the vapours of
degradation products which can arise on severe overheating of the materials or
during purging out should be avoided. Our Terluran safety data sheets give
further information.
Note
The information submitted in this publication is based on our current knowledge and
experience. In view of the many factors that may affect processing and application, these
data do not relieve processors of the responsibility of carrying out their own tests and
experiments; neither do they imply any legally binding assurance of certain properties or
of suitability for a specific purpose. It is the responsibility of those to whom we supply our
products to ensure that any proprietary rights and existing laws and legislation are
observed. In order to check the availability of products please contact us or our sales
agency.
BASF Company Ltd.
KCCI Bldg 14~16F
Namdaemunro 4 ga, Jung-gu
Seoul Korea 100-743
Internet address : http://www.basf-korea.co.kr
Terluran庐 HI-12
Test method Unit Value
Typical values at 23掳C for uncoloured products
ISO ASTM ISO ASTM
Mechanical properties
*
Tensile stress at yield / at break 40 40
527 D 638 MPa
Strain at yield 2.7 2.7
527 D 638 %
Strain at break 30
527 D 638 %
Young鈥檚 modulus 1900
527 D 638 MPa
Flexural strength 58
178 MPa
Flexural modulus 178 D 790-1 MPa
Shear modulus 6721-2 MPa
o o 2
Charpy impact strength 23 C / -30 C N.B./160
179/1eU KJ/m
o o 2
Charpy notched impact strength 23 C / -30 C 30/11
179/1eA KJ/m
o o
Izod notched impact strength 23 C / -30 C 31/11
180/1A Kg cm/cm
o o
Izod notched impact strength 23 C / -30 C 35
D 256-A Kg cm/cm
*
Ball indentation hardness , H 358/30 80
2039-1 MPa
Rockwell hardness, R scale 101
2039-2 D785 -
Thermal properties
o
Vicat softening temperature, VST/A/50 / VST/B/50 104 / 96
306 C
o
Deflection temp., 1.8Mpa(HDT A)/0.45Mpa(HDT B) 97 / 102
75-2 C
o
Max. service temperature 80
- C
-4
Thermal coefficient of linear expansion 0.8 鈥? 1.1
DIN53752 10 /K
Thermal conductivity 0.17
DIN 52612 W/(m鈰匥)
Processing
Melt volume rate MVR 220/10 14
1133 ml/10 min
o
Melt temperature range 230-260
C
o
Mold temperature 40 - 60
C
Mold shrinkage 0.4-0.7
%
Electrical properties
Dielectric constant at 100 Hz / 1MHz 2.9 / 2.8
IEC 250 -
-4
Dissipation factor at 100 Hz / 1 MHz 54 / 82
IEC 250 10
13
鈩? cm
Volume resistivity 10
IEC 93
鈩?
Surface resistivity IEC 93
CTI, solution A 600
IEC 112 -
Flammability
UL 94 (1.6 mm) 94HB
Class
UL 94 (3.2 mm) 94HB
Class
Automotive materials ( thickness d 鈮? 1 mm ) FMVSS 302 +
Miscellaneous properties
3
Density 1.02
1183 g/cm
Water absorption 1.03
62 %
o
Moisture absorption (23 C/50% r.h.) 0.21
62 %
NB : no break